Flip feram cell and method to form same

ABSTRACT

A method of forming an integrated ferroelectric/CMOS structure which effectively separates incompatible high temperature deposition and annealing processes is provided. The method of the present invention includes separately forming a CMOS structure and a ferroelectric delivery wafer. These separate structures are then brought into contact with each and the ferroelectric film of the delivery wafer is bonded to the upper conductive electrode layer of the CMOS structure by using a low temperature anneal step. A portion of the delivery wafer is then removed providing an integrated FE/CMOS structure wherein the ferroelectric capacitor is formed on top of the CMOS structure. The capacitor is in contact with the transistor of the CMOS structure through all the wiring levels of the CMOS structure.

DESCRIPTION

[0001] 1. Field of the Invention

[0002] The present invention relates to a ferroelectric random access memory (FERAM) cell, and in particular to a method of fabricating a ferroelectric (FE) capacitor on a complementary metal oxide semiconductor (CMOS) structure wherein exposure of the integrated structure to high temperature steps of FE deposition and processing is eliminated. The present invention also relates to a FERAM cell design and to a method to bond a FE capacitor to the CMOS structure after fabrication of both structures is complete, thereby avoiding the incompatibilities between the two processes. The resulting structure can be used as a non-volatile RAM (NVRAM) or a dynamic random access memory (DRAM), if the FE material is replaced with a material of high-dielectric-constant.

BACKGROUND OF THE INVENTION

[0003] The integration of high value capacitors in integrated circuits (ICs) is limited by the fact that conventional high value capacitors take up large areas of the IC chip, thus reducing device packing density and layout efficiency. Many applications require a large number of capacitors. Often the capacitors must be incorporated as discrete off-chip components, substantially increasing the bulk of the peripheral circuitry. In view of the increasing demand for compact lightweight electronic equipment, it is desirable that the number of discrete components be reduced.

[0004] The minimum dimensions of IC capacitors are determined primarily by the relatively low dielectric constant (0<10) of conventional capacitor dielectrics, e.g. SiO₂ and Si₃N₄. Thus, as device dimensions decrease, there is increasing interest in other dielectrics having higher dielectric constants than conventional dielectric materials.

[0005] Ferroelectric (FE) and high-epsilon (HE) dielectrics (0=20 or greater) have found application in random access memory (RAM) cells since they provide for the formation of NVRAMs and DRAMs. Moreover, when used as NVRAM, ferroelectric dielectrics advantageously provide low voltage programmability, fast access times and low power consumption.

[0006] FE materials pose several integration problems. In particular, most ferroelectric materials require high temperature post-deposition oxygen anneals (600° C. or above) to achieve properties desirable for storage media. However, such high anneal temperatures can be incompatible with the CMOS devices already fabricated on the wafer. Furthermore, any subsequent forming gas or hydrogen anneals (highly desirable for CMOS devices) degrade the ferroelectric material, thus requiring additional high temperature oxygen anneals late in the processing sequence which in turn are detrimental to the CMOS circuitry. In view of the above drawbacks with prior art methods of integrating ferroelectric capacitors with CMOS structures, there is a continued need for developing a new and improved method which is capable of providing an integrated FE capacitor/CMOS structure without subjecting the CMOS structure to high temperature steps that are typically required in the prior art for ferroelectric processing.

SUMMARY OF THE INVENTION

[0007] The present invention provides a method of integrating a FE capacitor with a CMOS structure which allows the CMOS structure to avoid potentially-detrimental high- temperature steps needed for FE deposition and processing. The invention likewise provides a method of integrating a plurality of FE capacitors with a plurality of CMOS structures. Specifically, the method of the present invention comprises the steps of:

[0008] (a) forming a CMOS structure in electrical contact with a conductive electrode layer on its exposed top surface;

[0009] (b) separately providing a ferroelectric delivery wafer, said ferroelectric delivery wafer comprising a sacrificial release layer formed on a delivery substrate, a conductive layer formed on said sacrificial release layer and a ferroelectric film formed on said conductive layer, said ferroelectric film having an exposed outer surface;

[0010] (c) placing said exposed outer surface of said ferroelectric film on the CMOS structure of step (a), wherein said ferroelectric film is in contact with said conductive electrode layer;

[0011] (d) bonding, at a temperature of less than about 600 EC, the outer surface of said ferroelectric film to said CMOS structure; and

[0012] (e) separating the sacrificial release layer from the bonded structure.

[0013] It is noted that the conductive electrode layer of the CMOS structure of step (a) may be patterned or unpatterned. Likewise, the conductive layer of the delivery wafer may also be patterned or unpatterned.

[0014] If not previously patterned, one or more of the conductive layers in the integrated FE capacitor/CMOS structure may optionally be patterned. This optional patterning step occurs after step (e) above. Another embodiment of the present method is to apply a surface treatment to the conductive electrode layer of the CMOS structure prior to conducting step (c). In yet another embodiment of the present invention, the method also includes a step of forming a passivating layer over the structure provided in step (e). In still a further embodiment of the present invention, the delivery wafer may include a second conductive layer on top of the ferroelectric film. In this embodiment of the invention, the second conductive layer may be patterned or unpatterned. In another aspect of the present invention, a novel integrated FE/CMOS structure is provided wherein the storage capacitor is constructed over all the transistors and wiring levels (excluding possibly any pad out structures) of the CMOS structure. Specifically, the novel integrated FE/CMOS structure of the present invention comprises:

[0015] a CMOS structure having at least one conductive layer and at least one transistor; and

[0016] a ferroelectric storage capacitor formed on said CMOS structure, said ferroelectric storage capacitor comprising a bottom conductive electrode, a layer of ferroelectric film and a top conductive electrode, wherein said bottom conductive electrode of said capacitor is connected to a terminal of said transistor through one or more conductive layers of said CMOS structure.

[0017] The present invention also provides a novel ferroelectric delivery wafer which allows for fabricating an integrated FERAM cell while isolating the CMOS circuitry from high temperature post-FE-deposition anneals. That is, although high temperature anneals are used in forming the separate CMOS and ferroelectric structures, and bonding thereof, no such anneals are needed thereafter. Specifically, the ferroelectric delivery wafer of the present invention comprises a carrier substrate, a sacrificial release layer formed on said carrier substrate, a conductive layer formed on said sacrificial release layer, and a ferroelectric film formed on said conductive layer. This structure is flipped onto a CMOS structure so that the ferroelectric film is in contact with a CMOS structure having an upper conductive electrode layer. After conducting steps (a) and (e) above, an integrated FE/CMOS structure in accordance with the present invention, is formed.

BRIEF DESCRIPTION OF THE DRAWINGS

[0018] FIGS. 1(a)-(e) are cross-sectional views illustrating the various processing steps that may be employed in one embodiment of the present invention. In this embodiment, the conductive layer of the ferroelectric delivery wafer is not patterned, whereas the conductive electrode layer of the CMOS structure is patterned.

[0019] FIGS. 2(a)-(j) are cross-sectional views illustrating different embodiments of the present invention. In FIGS. 2(a)-(b), neither the conductive layer of the FE delivery wafer nor the conductive layer of the CMOS structure is patterned prior to bonding. In FIGS. 2(c)-(d), only the conductive layer of the FE delivery wafer is patterned. In FIG. 2(e)-(f), the conductive layers of both the FE and CMOS structures are patterned. In FIGS. 2(g)-(h) and FIGS. 2(i)-(j), an unpatterned FE delivery wafer containing an additional conductive layer is bonded to an unpatterned and patterned CMOS wafer.

DETAILED DESCRIPTION OF THE INVENTION

[0020] The present invention will now be described in more detail by referring to the drawings that accompany the present application. It should be noted that in the accompanying drawings like reference numerals are used for describing like and corresponding elements.

[0021] Reference is first made to FIG. 1(a) which shows one possible CMOS structure that can be employed in the present invention. In this figure, the conductive electrode layer is patterned. In addition to a patterned conductive electrode layer in the CMOS structure, the present invention also contemplates a non-patterned conductive electrode layer such as those shown in FIGS. 2(a), (c), and 2(g). Although description is made to the structure shown in FIG. 1(a), it is noted herein that other CMOS structures containing at least one transistor and at least one conductive layer can be employed in the present invention.

[0022] Specifically, the CMOS structure shown in FIG. 1(a) comprises a semiconductor substrate 10 having diffusion regions, i.e. diffused portions of the bitlines, 12 formed in the surface thereof. On top of the semiconductor substrate there are shown transistor regions 14 which are in contact with the diffusion regions 12. The CMOS structure shown in FIG. 1(a) further comprises multiple wiring levels (or conductive layers) 16 which are formed in dielectric layer 18. The upper wiring level (or conductive layer) 16 u is composed of a patterned conductive electrode layer and it forms the bottom electrode of the integrated FE/CMOS structure of the present invention. Between the transistor regions, there is shown bitline 20 and bitline contact 22. It is emphasized that even though the figure depicts a patterned conductive electrode layer as 16 u, 0the present invention also contemplates the use of a non-patterned conductive electrode layer 16 u, as shown in FIGS. 2(a), 2(c) and 2(g).

[0023] The structure shown in FIG. 1(a) is composed of materials well known to those skilled in the art and it is fabricated using conventional processes well known to those skilled in the art. For example, semiconductor substrate 10 is composed of any semiconducting material including, but not limited to: Si, Ge, SiGe, GaAs, InAs, InP, all other III/V compounds and organic semiconductors. The semiconductor substrate may be doped or undoped. The diffusion regions may contain p or n type dopants.

[0024] The transistor region is comprised of a conventional gate stack which includes a layer of gate insulator such as SiO₂ formed on the surface of the semiconductor substrate and a layer of polysilicon or other gate conductor formed on the gate insulator. A salicide layer may be formed on top of the polysilicon or gate conductor. Transistor region 14 may be separated by sidewall isolation regions as well as other conventional components well known to those skilled in the art. For simplicity, the various elements of the transistor are not shown in the drawings, but are nevertheless intended to be included in region 14.

[0025] Wiring levels 16 comprise vias and lines which contain conventional conductive materials such as metals, noble-metals, conductive nitrides, noble metal oxides, conductive oxides and mixtures or multilayers thereof. Exemplary conductive materials include: Cu, W, Al, Pt, polysilicon, TiN, Ta, TaN, Ti and WSi_(x). The various wiring levels may be composed of the same or different conductive material. In FIG. 1(a), all the wiring levels (lines and vias) are depicted as being composed of the same conductive materials.

[0026] Dielectric layer 18 is composed of any inorganic or organic dielectric material known to the art including, but not limited to: SiO₂, Si₃N₄, SiCOH, diamond-like carbon, paralyene polymers, polyimides, silicon-containing polymers, organic polymers, hybrid organo-silicon polymers (HOSP) and other suitable dielectric materials. Dielectric layer 18 may be composed of layers of the same material, as shown in FIG. 1(a), or layers of different dielectric materials (not shown). When layers of different dielectric materials are used, a barrier layer, not shown in the drawings, may be formed between each successive wiring level. The optional barrier layer is composed of conventional materials including, but not limited to: SiO₂, A1 ₂O₃, TiO₂, Si₃N₄, SiO_(x)N₄ and Ta₂O₅.

[0027] As stated above, the structure shown in FIG. 1(a) is fabricated using conventional processing steps which are well known to those skilled in the art including: semiconductor device fabrication and back end of the line (BEOL) processing. For example, the CMOS device shown in FIG. 1(a) can be fabricated by forming the transistor region on the surface of the semiconductor substrate, i.e. growing a gate insulator, depositing a gate conductor on said gate insulator and thereafter patterning those layers to provide the transistor region. The diffusion regions can then be formed using conventional ion implantation and annealing.

[0028] Although the drawings of the present invention depict doing all BEOL wiring before bonding the wafers, it is also within the contemplation of the present invention to carry out wiring after bonding.

[0029] The wiring levels of the CMOS structure shown in FIG. 1(a) are then typically formed by: depositing a dielectric material on the surface of the semiconductor structure, opening vias in the dielectric layer, filling the vias with a conductive material, forming trenches in the dielectric layer over the vias, filling the trenches with a conductive material, and planarizing the structure using conventional planarization techniques such as chemical-mechanical polishing or grinding. It is noted that in this figure, the last, i.e. upper, wiring level 16 u is a patterned conductive electrode comprising a conductive electrode material. The conductive electrode layer 16 u is the bottom electrode of the integrated FE/CMOS structure of the present invention.

[0030] Suitable conductive electrode materials that can be used in the present invention as the upper conductive layer of the CMOS structure include, but are not limited to: noble metals such as Pt, Pd, Ir, Rh, Os, Au, Ag, and Ru; noble metal oxides such as PtO_(x), IrO_(x), PdO_(x), RhO_(x), OsO_(x), AuO_(x), AgO_(x) and RuO_(x); conducting oxides such as SrRuO₃, LaSrCoO₃, YBa₂Cu₃O₇; non-noble metals; conducting silicides; doped polycrystalline silicon; mixtures and multilayers thereof. The noble metals and/or oxides may be crystalline or in an amorphous form. As stated above, the upper conductive electrode layer of the CMOS structure may be patterned using conventional lithography and RIE or unpatterned.

[0031] The upper conductive layer of the CMOS structure may further include an additional layer of a consumable material which can subsequently react with one or more layers of the ferroelectric delivery wafer during bonding. This consumable layer may be conductive, semiconducting, or insulating, and patterned before or after said step of bonding. The consumable layer is preferably formed from a material such as doped or undoped polycrystalline silicon which may react with a metal layer to form a conductive metal silicide.

[0032] It is noted that bitline and bitline contacts, 20 and 22 respectively, are composed of conductive materials and may be fabricated in the same manner as the various wiring levels.

[0033] After forming the conductive electrode layer 16 u, which may include planarization, the structure may optionally be subjected to an appropriate surface treatment step. Suitable surface treatments that may optionally be employed in the present invention include: oxidation by plasma ashing, thermal oxidation, surface chemical treatments and application of a thin metal oxide layer by chemical solution deposition (CSD), chemical vapor deposition (CVD) or physical vapor deposition (PVD).

[0034] When oxidation by plasma ashing is performed, it may be carried out using high density plasma, microwave plasma, RF plasma ion beam bombardment produced by an oxygen-containing ion beams, or combination thereof, with or without separately controllable biasing. Typically, when employed, plasma ashing is conducted in a reaction chamber having an oxygen pressure between about 0.01 to about 2000 mTorr, a radio frequency power of at least 50 W and an exposure time of at least 1 second.

[0035] When thermal oxidation is employed as the surface treatment means, the oxidation is typically carried out a temperature of less than about 600 EC. The thermal oxidation may include: HCl, H₂O or H₂O₂ to enhance hydroxyl formation. Suitable oxidizing gases include: O₂, N₂O, O₃ or combination thereof.

[0036] When surface chemical treatments are employed as the optional surface treatment means, acids such as HNO₃, H₂SO₄ and aqua regia; bases; and peroxide washes may be employed.

[0037] In accordance with the present invention, a ferroelectric delivery wafer is prepared separately from the CMOS structure shown in FIG. 1(a). One possible ferroelectric delivery wafer of the present invention is shown in FIG. 1(b). Specifically, the delivery wafer comprises a carrier substrate 24, a sacrificial release layer 26 formed on said carrier substrate, a conductive layer 28 formed on the sacrificial release layer, and a ferroelectric film 30 formed on the conductive layer. The conductive layer 28 may be patterned as shown in 2(d) and 2(f) or non-patterned as shown in FIG. 1(b), 2(b), 2(h) and 2(j). If patterned, conductive layer 28 of FIG. 2(f) is preferably embedded in dielectric layer 29 to insure planarity of the ferroelectric delivery wafer. In another embodiment of the present invention, an optional second conductive layer 34 is formed on the ferroelectric film as shown in FIGS. 2(h) and 2(j).

[0038] A suitable anneal may be performed at this time to achieve desired ferroelectric properties. Typically, such an anneal is carried out at a temperature of about 600° C. or above.

[0039] Carrier substrate 24 may be composed of one of the semiconducting materials described for semiconductor substrate 10 or it may be composed of a dielectric material like the kind mentioned above for dielectric layer 18. The carrier substrate could also be a material with its thermal-expansion coefficient well-matched to Si. Some ceramics exhibit this property. Likewise, conductive layer 28, which forms the top electrode of the capacitor of the present invention, and the optional second conductive layer 34 comprise one or more of the previously mentioned metals, noble metals, conductive nitrides, noble metal oxides, conductive oxides, conducting suicides, doped polycrystalline silicon, mixtures and multilayers thereof, which are used in forming conductive layers 16 in the CMOS structure.

[0040] Second conductive layer 34 of the ferroelectric delivery wafer may further include an additional layer of a consumable material which can subsequently react with one or more layers of the CMOS structure during bonding. This consumable layer may be conductive, semiconducting, or insulating, and patterned before or after said step of bonding. The consumable layer is preferably formed from a material such as doped or undoped polycrystalline silicon which may react with a metal layer to form a conductive metal silicide. While a consumable bonding layer may be present on either the ferroelectric delivery wafer or the CMOS structure prior to bonding, a preferable embodiment comprises an oxidation-resistant silicide-forming metal such as Pt or Ir as the optional second conductive material of the ferroelectric delivery wafer, and a thin (5-50 nm) consumable polycrystalline silicon layer on the CMOS structure.

[0041] Sacrificial release layer 26 may be an etch stop layer (for the situation in which the delivery wafer substrate is removed by etching). It may also be a surface layer of the delivery substrate that has been ion-implanted (before or after the ferroelectric deposition) with species such as hydrogen that become volatile upon heating. It may also be a deposited layer that is preferably thermally stable at the ferroelectric decomposition temperature, and easily selectively etched or decomposed without damage to the ferroelectric or conductive layers. Suitable deposited sacrificial release layers include, but are not limited to: GeO₂, W, TiN, IrO₂ PdO, and WSi₂.

[0042] Sacrificial release layer 26 may further include an optional passivation layer to protect the transferred layers against the damaging conditions of the releasing process. This optional layer would typically be transferred with the ferroelectric and electrode layers, and be used in cases where the release process entailed exposure to hydrogen or other reducing species. Optional passivation layer materials include: A1 ₂ 0 ₃, TiO₂, Ta₂O₅, Si₃N₄, and SiO₂.

[0043] The ferroelectric film that is employed as element 30 of the delivery element of the present invention is a crystalline, polycrystalline or amorphous high dielectric constant material (0=20 or above). Suitable ferroelectric materials that can be employed in the present invention include, but are not limited to: the perovskite-type oxides, layered ferroelectrics, compounds containing pyrochlore structures such as Cd₂Nb₂O₇, potassium dihydrogen phosphates, phosphates of rubidium, cesium or arsenic and other like ferroelectric materials. Combinations of these ferroelectric materials or multilayers are also contemplated herein. High-epsilon materials may also be employed in the present invention as the high dielectric ferroelectric material. The high dielectric material may display a spontaneous electric polarization (for NVRAM) or not (DRAM).

[0044] Of the aforementioned ferroelectric materials, it is highly preferred that the ferroelectric film of the present invention be composed of a perovskite-type oxide. The term Aperovskite-type oxide@ is used herein to denote a material which includes at least one acidic oxide containing at least one metal from Group IVB (Ti, Zr or Hf), VB (V, Nb or Ta), VIB (Cr, Mo or W), VIIB (Mn or Re), IIIA (Al, Ga or In) or IB (Cu, Ag or Au) of the Periodic Table of Elements (CAS version) and at least one additional cation having a positive formal charge of from about 1 to about 3. Such perovskite-type oxides typically have the basic formula: ABO₃ wherein A is one of the above mentioned cations, and B is one of the above mentioned metals which forms the acidic oxide.

[0045] Suitable perovskite-type oxides include, but are not limited to: titanate-based ferroelectrics, manganate-based materials, cuprate-based materials, tungsten bronze-type niobates, tantalates, or titanates, and bismuth layered-tantalates, niobates or titanates. Of these perovskite-type oxides, it is preferred to use strontium bismuth tantalate, strontium bismuth niobate, bismuth titanate, strontium bismuth tantalate niobate, lead zirconate titanate, lead lanthanum zirconate titanate, and compositions of these materials modified by the incorporation of dopants as the ferroelectric material.

[0046] The ferroelectric wafer structure shown in FIG. 1(b) is formed using conventional deposition processes well known to those skilled in the art. For example, layers 26 and 28 of the delivery wafer may be formed by chemical vapor deposition (CVD), plasma-assisted CVD, sputtering, reactive sputtering, pulsed-laser deposition, chemical solution deposition, physical-vapor deposition, plating and other like deposition techniques. After deposition of each layer, the structure may optionally be planarized using conventional techniques such as chemical-mechanical polishing.

[0047] The ferroelectric film is also formed using conventional deposition techniques well known to those skilled in the art including, but not limited to: chemical solution deposition (CSD), sol gel, metal-organic decomposition, spin coating, sputtering, reactive sputtering, metal-organic chemical vapor deposition, physical vapor deposition, plasma-assisted chemical vapor deposition, pulsed laser deposition, chemical vapor deposition, evaporation and like deposition techniques. A high temperature anneal may need to be performed at this time to obtain desired ferroelectric properties.

[0048] After forming the structure shown in FIG. 1(b), the ferroelectric delivery wafer is placed in proximity to the CMOS structure of FIG. 1(a) so that ferroelectric film 30 is in contact with patterned conductive electrode layer 16 u and the top surface of dielectric layer 18. This intermediate structure is shown in FIG. 1(c).

[0049] In one embodiment of the present invention, the ferroelectric delivery wafer is optionally treated with one of the above mentioned surface treatments prior to bonding. In embodiments wherein a patterned conductive layer is employed in the delivery wafer, an alignment process may be necessary to ensure proper placement of the delivery wafer on the CMOS structure.

[0050] The intermediate structure of FIG. 1(c) is then bonded at a temperature of less than about 600° C. so that bonding occurs between ferroelectric film 30 and the top dielectric layer of the CMOS structure as well as patterned conductive electrode layer 16 u. Specifically, the annealing step is carried out in a substantially inert gas atmosphere, e.g. vacuum, He, Ar, N₂, or mixtures thereof that can be optionally mixed with an oxidizing gas such as O₂, steam, O₃, N₂O or H₂O₂. Highly preferred annealing temperatures that can be employed in the present invention are from about room temperature, i.e. 25 EC, to about 600 EC, with from about 100° to about 400° C. being more highly preferred. Typically, annealing is carried out for a time period of from about 1 minute to about 6 hours, with from about 2 minutes to about 3 hours being more highly preferred. The annealing step may be carried out using a single ramp cycle or multiple ramp and soak cycles can also be used.

[0051] Bonding may be additionally facilitated using external pressure to push the bonding interfaces together, and/or by using the surface tension of a thin, removable liquid layer placed at the bonding interface. The thin liquid layer would typically be water, and could be removed by evaporation. Bonding may also be facilitated with the use of electric fields in processes known to the prior art as anodic bonding.

[0052] After bonding ferroelectric film 30 to the CMOS structure, sacrificial release layer 26 and carrier substrate 24 are removed from the structure, See FIG. 1(d). The preferred method for removing the carrier substrate depends on the type of sacrificial release layer selected. One means of removing the carrier wafer is by a selective etch process.

[0053] It is noted that in this figure, the ferroelectric film is bonded to the CMOS dielectric and the upper conductive electrode layer. In accordance with the present invention, the upper conductive electrode layer 16 u of the CMOS structure becomes the bottom electrode of the storage capacitor. On top of the ferroelectric film is the upper electrode 28 of the capacitor. As further shown in FIG. 1(d), the capacitor, i.e. upper conductive electrode layer (bottom electrode) 16 u, ferroelectric film 30 and conductive layer (upper electrode) 28, is formed over the CMOS structure. In cases wherein the conductive electrode layer 16 u of the CMOS is not patterned in FIGS. 2(a), 2(c) and 2(g), ferroelectric film 30 would be directly bonded to the unpatterned conductive layer. In cases where the optional conductive layer is present on the FE delivery wafer, the optional conductive layer would be bonded to the CMOS wafer.

[0054] After removing at least most of the carrier substrate 24 and the sacrificial release film 26, the resulting integrated CMOS/FE structure may be optionally polished. Additional electrode and/or ferroelectric patterning steps may then be performed as required for electrical isolation of individual capacitor elements. A passivating material 32, as shown in FIG. 1(e), may then be optionally formed on the surface of conductive layer 28. Suitable passivating materials include: A1 ₂O₃, TiO₂, Ta₂O₅, Si₃N₄ and SiO₂. The passivating material layer is formed using conventional deposition processes well known to those skilled in the art including, but not limited to: CVD, dip coating and spin-on coating. The thickness thereof is sufficient to prevent diffusion of air or moisture into the underlying layers of the integrated FE/CMOS structure.

[0055] While the present invention has been particularly shown and described with respect to preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in form and detail may be made without departing from the spirit and scope of the present invention. 

Having thus described our invention, what we claim as new and desire to secure by the letters patent is:
 1. A method of fabricating an integrated FE/CMOS structure comprising the steps of: (a) forming a CMOS structure in electrical contact with a conductive electrode layer; (b) separately providing a ferroelectric delivery wafer, said ferroelectric delivery wafer comprising a sacrificial release layer formed on a delivery substrate, a conductive layer formed on said sacrificial release layer and a ferroelectric film formed on said conductive layer, said ferroelectric film having an exposed outer surface; (c) placing said exposed outer surface of said ferroelectric film on the CMOS structure of step (a), wherein said ferroelectric film is in contact with said conductive electrode layer; (d) bonding, at a temperature of less than about 600□ C., the outer surface of said ferroelectric film to said CMOS structure; and (e) separating the sacrificial release layer from the bonded structure.
 2. The method of claim 1 further comprising: (f) optionally performing additional steps required for electrical isolation of individual capacitor elements.
 3. The method of claim 1 wherein a passivating layer is formed over the structure provided in step (e).
 4. The method of claim 1 wherein said conductive electrode layer of said CMOS structure is patterned or unpatterned.
 5. The method of claim 1 wherein said conductive layer of said ferroelectric delivery wafer is patterned or unpatterned.
 6. The method of claim 1 further comprising a surface treatment step to said conductive electrode layer and/or said ferroelectric film prior to step (c).
 7. The method of claim 1 wherein said delivery wafer of step (c) further includes a second conductive layer over said ferroelectric film, and said placing and bonding of steps (c) and (d) entails the exposed outer surface of said second conductive layer instead of said FE layer.
 8. The method of claim 7 wherein said second conductive layer is patterned before or after said step of bonding.
 9. The method of claim 1 wherein said CMOS structure further comprises a transistor region formed on top of a semiconductor substrate.
 10. The method of claim 9 wherein said semiconductor substrate is a semiconducting material selected from the group consisting of Si, Ge, SiGe, GaAs, InAs, InP, other III/V compounds and organic semiconductors.
 11. The method of claim 1 wherein said carrier substrate is a semiconducting material or a dielectric material.
 12. The method of claim 1 wherein said conductive electrode layer of said CMOS structure is composed of a conductive material selected from the group consisting of a metal, a noble metal, a noble metal oxide, a conductive oxide, a conductive nitride, a conductive silicide, a doped polycrystalline silicon, and mixtures and multilayers thereof.
 13. The method of claim 12 wherein said conductive layer further includes a consumable reaction layer which may be conductive or non-conductive.
 14. The method of claim 13 wherein said consumable reaction layer is composed of doped or undoped polycrystalline silicon.
 15. The method of claim 1 wherein said conductive layer of said ferroelectric delivery wafer is composed of a metal, a noble metal, a noble metal oxide, or mixtures and multilayers thereof.
 16. The method of claim 7 wherein said conductive layer of said delivery wafer is composed of a conductive material selected from the group consisting of a metal, a noble metal, a noble metal oxide, a conductive oxide, a conductive nitride, a conductive silicide, doped polycrystalline silicon, and mixtures and multilayers thereof.
 17. The method of claim 7 wherein said second conductive layer of said delivery wafer further includes a consumable reaction layer which may be conductive or non-conductive.
 18. The method of claim 17 wherein said consumable reaction layer is composed of doped or undoped polycrystalline silicon.
 19. The method of claim 1 wherein said ferroelectric film is selected from the group consisting of a perovskite-type oxide, a layered ferroelectric, a compound containing a pyrochlore structure, potassium dihydrogen phosphate and a phosphate of rubidium, cesium or arsenic.
 20. The method of claim 19 wherein said ferroelectric material is a perovskite-type oxide having the formula ABO₃ wherein B is at least one acidic oxide containing a metal from Group IVB, VB, VIB, IIIA, VIIB or IB of the Periodic Table of Elements, and A is at least one additional cation having a positive formal charge of from about 1 to about
 3. 21. The method of claim 20 wherein said perovskite-type oxide is a titanate-based ferroelectric, a manganate-based material, a cuprate based material, a tungsten bronze-type niobate, tantalate or titanate, or a layered bismuth tantalate, niobate or titanate.
 22. The method of claim 21 wherein said ferroelectric film is composed of a ferroelectric material selected from the group consisting of bismuth titanate, strontium bismuth tantalate, strontium bismuth niobate, strontium bismuth tantalate niobate, lead zirconate titanate, lead lanthanum zirconate titanate and compositions of these materials modified by incorporation of a dopant.
 23. The method of claim 1 wherein step (d) is carried out in vacuum or in a substantially inert gas atmosphere, said inert gas atmosphere being selected from the group consisting of He, Ar, N₂, and mixtures thereof.
 24. The method of claim 1 wherein step (d) is carried out at a temperature of from about 25° to about 600° C. for a time period of from about 1 minute to about 6 hours.
 25. The method of claim 24 wherein step (d) is carried out at a temperature of from about 100° to about 400° C. for a time period of from about 2 minutes to about 3 hours.
 26. The method of claim 1 wherein said sacrificial release layer is selected from the group consisting of GeO₂, W, TiN, IrO₂, PdO and WiSi₂.
 27. The method of claim 1 wherein said sacrificial release layer of step (b) is provided by implanting said delivery wafer with a desorbable species prior to or after deposition of said ferroelectric layer.
 28. The method of claim 27 wherein said desorbable species is hydrogen.
 29. An integrated FE/CMOS structure comprising a CMOS structure having at least one conductive layer and a transistor; and a ferroelectric storage capacitor formed on said CMOS structure, said ferroelectric storage capacitor comprising a bottom conductive electrode, a layer of ferroelectric film and a top conductive electrode, wherein said bottom conductive electrode of said capacitor is connected to a terminal of said transistor through one or more of said conductive layers of said CMOS structure.
 30. The integrated FE/CMOS structure of claim 29 wherein said CMOS structure further includes a semiconductor substrate.
 31. The integrated FE/CMOS structure of claim 30 wherein said semiconductor substrate is a semiconducting material selected from the group consisting of Si, Ge, SiGe, GaAs, InAs, InP, other III/V compounds, and organic semiconductors.
 32. The integrated FE/CMOS structure of claim 29 wherein said top and bottom conductive electrodes are composed of the same or different conductive materials, said conductive materials are selected from the group consisting of metals, noble metals, noble metal oxides, conductive oxides, conductive nitrides, doped polycrystalline silicon, conductive metal suicides and mixtures or multilayers thereof.
 33. The integrated FE/CMOS structure of claim 29 wherein said ferroelectric film is selected from the group consisting of a perovskite-type oxide, a layered ferroelectric, a compound containing a pyrochlore structure, potassium dihydrogen phosphate and a phosphate of rubidium, cesium or arsenic.
 34. The integrated FE/CMOS structure of claim 33 wherein said ferroelectric material is a perovskite-type oxide having the formula ABO3 wherein B is at least one acidic oxide containing a metal from Group IVB, VB, VIB, VIIB, IIIA or IB of the Periodic Table of Elements, and A is at least one additional cation having a positive formal charge of from about 1 to about
 3. 35. The integrated FE/CMOS structure of claim 34 wherein said perovskite-type oxide is a titanate-based ferroelectric, a manganate-based material, a cuprate based material, a tungsten bronze-type niobate, tantalate or titanate, or a layered bismuth tantalate, niobate or titanate.
 36. The integrated FE/CMOS structure of claim 35 wherein said ferroelectric film is composed of a ferroelectric material selected from the group consisting of bismuth titanate, strontium bismuth tantalate, strontium bismuth niobate, strontium bismuth tantalate niobate. lead zirconate titanate, lead lanthanum zirconate titanate and compositions of these materials modified by incorporation of a dopant.
 37. The integrated FE/CMOS structure of claim 29 wherein said top and bottom electrodes are patterned or unpatterned.
 38. A FE delivery wafer comprising a carrier substrate, a sacrificial release layer formed on said carrier substrate, a conductive layer formed on said sacrificial release layer and a ferroelectric film formed on said conductive layer.
 39. The FE delivery wafer of claim 38 wherein said carrier substrate is a semiconducting material or a dielectric material.
 40. The FE delivery wafer of claim 39 wherein said semiconducting material is Si, Ge, SiGe, GaAs, InAs, InP, another III/V compound or an organic semiconductor.
 41. The FE delivery wafer of claim 39 wherein said dielectric material is an inorganic or organic dielectric material selected from the group comprising SiO₂, Si₃N₄, SiCOH, diamond-like carbon, paralyene polymers, polyimides and silicon-containing polymers, organic polymers, and hybrid organo-silicon polymers (HOSP).
 42. The FE delivery wafer of claim 38 further comprising a second conductive layer formed on said ferroelectric film.
 43. The FE delivery wafer of claim 38 wherein said ferroelectric film is composed of a perovskite-type oxide, a layered ferroelectric, a compound containing a pyrochlore structure, potassium dihydrogen phosphate or a phosphate of rubidium, cesium or arsenic.
 44. The FE delivery wafer of claim 43 wherein said ferroelectric material is a perovskite-type oxide having the formula ABO₃ wherein B is at least one acidic oxide containing a metal from Group IVB, VB, VIB, VIIB, IIIA or IB of the Periodic Table of Elements, and A is at least one additional cation having a positive formal charge of from about 1 to about
 3. 45. The FE delivery wafer of claim 44 wherein said perovskite-type oxide is a titanate-based ferroelectric, a manganate-based material, a cuprate based material, a tungsten bronze-type niobate, tantalate or titanate, or a layered bismuth tantalate, niobate or titanate.
 46. The FE delivery wafer of claim 45 wherein said ferroelectric film is composed of a ferroelectric material selected from the group consisting of bismuth titanate, strontium bismuth tantalate, strontium bismuth niobate, strontium bismuth tantalate niobate, lead zirconate titanate, lead lanthanum zirconate titanate and compositions of these materials modified by incorporation of a dopant.
 47. The FE delivery wafer of claim 38 wherein said sacrificial release layer selected from the group consisting of GeO₂, W, TiN, IrO₂, PdO and WSi₂.
 48. The FE delivery wafer of claim 38 wherein said sacrificial release layer is provided by implanting said delivery wafer with a desorbable species prior to or after deposition.
 49. The FE delivery wafer of claim 48 wherein said desorbable species is hydrogen.
 50. The FE delivery wafer of claim 38 wherein said conductive layer is patterned or non-patterned. 